Effect of Doping of Organic and In-organic Acids on Polyaniline/ Mn3O4 Composite for NTC & Conductivity Behavior

Singla, M.L. and Awasthi, Sajeela and Srivastava, Alok and Jain, D.V.S. (2007) Effect of Doping of Organic and In-organic Acids on Polyaniline/ Mn3O4 Composite for NTC & Conductivity Behavior. Sensors and Actuators A: Physical , 136 (2). pp. 604-612. ISSN 0924-4247

Full text not available from this repository.
Official URL: http://www.sciencedirect.com/science/article/pii/S...

Abstract

The paper deals with the study of TCR and conductivity behaviour of the PANI/Mn3 O4 composite in its emeraldine salt state doped with different acids like H3PO4, H2SO4, HClO4, CH3COOH and CH2=CHCOOH. The conductivity results have also been compared with pure emeraldine salt doped with same acid. The characterisation of each composite sample and emeraldine salt was done using XRD, FT-IR, and TGA. From the TCR studies it has been observed that PANI/Mn3O4 composite doped with acetic acid and acrylic acid have negative temperature co-efficient (NTC) behaviour in the temperature range 20-110 and 20-160°C, respectively. Thermistors constant (B) values calculated from the data are 3625 K-1 for composite doped with acetic acid and 3745 K-1 for acrylic acid. Composite samples doped with H3PO4, H2SO4 and HClO4 acid did not show NTC behaviour, as the thermistor constant values in these composites are found to be on lower side. The results of the conductivity behaviour for the composite doped with CH3COOH and HClO4 are of the same order as that of doped emeraldine salt, whereas in other three composite samples the conductivity is much lower in comparison to emeraldine salt samples. XRD studies reveal that crystalline PANI/Mn3O4 composite has been transformed into amorphous phase during doping. From FT-IR spectra, it can be concluded that adsorbed acids anion on the oxide surface work as the charge compensator for positive charge on PANI. TG curves of composite suggest that the thermal degradation process of PANI/Mn3O4 composite proceeds in three steps and thermal stability of the composite depend on the dopant acid. The improvement in the thermal stability of composite is attributed to the interaction between a specific acid and PANI/Mn3O4 composite which may restrict the thermal motion of the PANI chain and shield the degradation of PANI in the composite. From the above study it can be concluded that the PANI/Mn3O4 composite doped with organic acids has the potential to act as NTC material for thermistor applications. Due to variation in the conductivity behaviour of doped composites and PANI, it may find application as sensing material.

Item Type: Article
Uncontrolled Keywords: PANI/Mn3O4 composite; Doping; NTC; Conductivity
Subjects: CSIO > Chemistry
Depositing User: Ms. Narinder Kaur
Date Deposited: 05 Mar 2012 12:23
Last Modified: 05 Mar 2012 12:23
URI: http://csioir.csio.res.in/id/eprint/99

Actions (login required)

View Item View Item